Pengaruh Penekanan Pellet Silika Terhadap Sifat Mekanik (Hardness) Dan Porositas Serta Mikrostruktur Plat Panel Keramik Komposit

Chandra, Nindy (2021) Pengaruh Penekanan Pellet Silika Terhadap Sifat Mekanik (Hardness) Dan Porositas Serta Mikrostruktur Plat Panel Keramik Komposit. Other thesis, Universitas Islam Riau.

[img]
Preview
 Text
143310248.pdf
Download (2MB) | Preview

Abstract

Composite ceramic panel plate (PPKK) is one type of composite product/ceramic panel made of particles bonded with a binder or matrix and then cold pressed. Reinforcement is added by binders with the aim of improving mechanical properties by spreading the stresses between the fibers and the matrix. This study aims to determine the mechanical properties (hardness), porosity and microstructure of the composite ceramic panel plate. In this study, the selected composite material was silica and the composite matrix was polyethylene glycol (PEG) 400 and was given pressure variations of 3 Tons, 4 Tons and 5 Tons. The printed composite ceramic panel plate (PPKK) was tested for hardness (Brinell) to determine the value of the hardness of the composite, and a porosity test was carried out to determine the percentage (%) of porosity in the composite which was printed under compression and observed the microstructure using an optical microscope. Olympus with x50 magnification to see the cavities that appear due to the com

Item Type: Thesis (Other)
Contributors:
ContributionContributorsNIDN/NIDK
SponsorKarni, Dediperpustakaan@uir.ac.id
Uncontrolled Keywords: Composite Ceramic Panel Plate Mechanical Properties Porosity Microstructure
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: > Teknik Mesin
Depositing User: Febby Amelia
Date Deposited: 19 Mar 2022 03:44
Last Modified: 19 Mar 2022 03:44
URI: http://repository.uir.ac.id/id/eprint/9018

Actions (login required)

View Item View Item
Repository Universitas Islam Riau is powered by EPrints 3 which is developed by the School of Electronics and Computer Science at the University of Southampton. More information and software credits.